パルス中性子応力測定法による超音波衝撃処理した十字溶接継手の残留応力評価

DOI Web Site 参考文献4件

書誌事項

タイトル別名
  • Residual stress evaluation by pulsed neutron stress measurement for cruciform welded joints treated with ultrasonic impact method

抄録

<p>The residual stress state inside the cruciform welded joints were measured using the pulsed neutron stress measurement method. The points of interest in this study are the weld toe and its interior. We also compared the cases with and without ultrasonic impact treatment (UIT), which is expected as a fatigue strength improvement technology. Furthermore, the case where tensile stress or compressive stress was applied after UIT treatment was also examined. The applied stresses at this time were 75 % or 85 % of the yield point, respectively. From the above, we considered the cause of the change in the residual stress on the surface after UIT treatment, which was clarified in the preliminary experiment, in the early stage of fatigue. As a result, the load after the UIT treatment caused plastic deformation in a part of the inside, which caused the redistribution of residual stress. It was also found that such changes in the internal residual stress state are the cause of the changes in the surface residual stress.</p>

収録刊行物

参考文献 (4)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ