- Coherency evaluation of <i>α</i>-Mg/C15-Al<sub>2</sub>Ca interface for a Mg-Al-Ca alloy
- Mg-Al-Ca合金におけるα-Mg/C15-Al₂Ca界面の整合性評価
- Mg-Al-Ca ゴウキン ニ オケル a-Mg/C15-Al ₂ Ca カイメン ノ セイゴウセイ ヒョウカ
この論文をさがす
抄録
<p>The C15-Al2Ca precipitates were observed using high-resolution transmission electron microscopy (HRTEM) to identify the coherency of the α-Mg/C15-Al2Ca interface for the Mg-5Al-1.5Ca alloy aged at the temperature range from 548 to 598 K. The α/C15 coherent interface turned to the semi-coherent one by the introduction of misfit dislocations on the planar surface of the C15 precipitates for the alloy aged at 598 K for 1 h, whereas the coherency was maintained for the alloy aged at 548 K for 10 h. The curve showing the loss of interface coherency was drawn in the TTP diagram for the Mg-5Al-1.5Ca alloy, which is indicated that the α/C15 interface coherency has remained within 3.6×107 s (10000 h) at 500 K.</p>
収録刊行物
-
- 軽金属
-
軽金属 71 (2), 127-129, 2021-02-15
一般社団法人 軽金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390850313411740800
-
- NII論文ID
- 130007998316
-
- NII書誌ID
- AN00069773
-
- ISSN
- 18808018
- 04515994
-
- NDL書誌ID
- 031282135
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可