Graphitization Behaviors of Creep-ruptured 0.3% Carbon Steel at 673 to 773 K
-
- Hatakeyama Tomotaka
- International Center for Young Scientists, National Institute for Materials Science
-
- Sawada Kota
- Research Center for Structural Materials, National Institute for Materials Science
-
- Sekido Kaoru
- Research Center for Structural Materials, National Institute for Materials Science
-
- Hara Toru
- Research Network and Facility Services Division, National Institute for Materials Science
-
- Kimura Kazuhiro
- Research Center for Structural Materials, National Institute for Materials Science
抄録
<p>Graphitization in carbon steels must be prevented because it reduces the amount of carbon in the matrix, which degrades the material performance due to loss in strength. In addition, when graphite particles are aligned, they can cause fracture by their linkage. The safety management standards for carbon steels in high-temperature applications state that graphitization should be considered at 698 K and above. The number of reported cases on graphitization in steels below 698 K is limited, and the mechanism has not yet been well investigated. This paper reports the finding of unprecedented graphitization at 673 K in creep-ruptured carbon steel and an elongated form of graphite that appears after a much shorter time at 673–773 K than other previously reported times. Furthermore, the formation mechanism of this elongated graphite is discussed. Dislocations and inclusions in the vicinity of grain boundaries may facilitate graphitization kinetics at these temperatures.</p>
収録刊行物
-
- ISIJ International
-
ISIJ International 61 (3), 993-1001, 2021-03-15
一般社団法人 日本鉄鋼協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390850323950183040
-
- NII論文ID
- 130007999467
-
- ISSN
- 13475460
- 09151559
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可