- Electrochemical Degradation Resistance of Pt/TiN/C Cathode Catalysts for Polymer Electrolyte Fuel Cells prepared using the Polygonal Barrel-Sputtering Method
この論文をさがす
抄録
Electrochemical degradation resistance of carbon-supported Pt and TiN (Pt/TiN/C) cathode catalysts for polymer electrolyte fuel cells prepared using the polygonal barrel-sputtering method was investigated. The characterization of the prepared carbon-supported TiN (TiN/C) samples showed that TiN nanoparticles were uniformly deposited on the surfaces of the carbon particles. Subsequently, Pt/TiN/C catalysts were prepared by sputtering Pt on the TiN/C samples. The change in electrochemical surface areas (ESAs) of the obtained samples was evaluated by successive potential cycling. As compared with the carbon-supported Pt catalyst, the Pt/TiN/C catalyst with the amount of TiN deposited of 10 wt.% showed smaller ESA reduction after 100th potential cycling. The effects of TiN on the ESA reduction became greater by increasing the amount of deposited TiN from 10 to 24 wt.%, although the ESA absolute values decreased. These results demonstrate that TiN deposition is useful to prevent ESAs from reduction and improve the durability of PEFCs.
収録刊行物
-
- 富山大学水素同位体科学研究センター研究報告
-
富山大学水素同位体科学研究センター研究報告 33 29-34, 2014-06-30
富山大学水素同位体科学研究センター
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390853649736556672
-
- NII論文ID
- 120005456370
-
- NII書誌ID
- AA11841872
-
- ISSN
- 13463675
-
- HANDLE
- 10110/12847
-
- NDL書誌ID
- 025633745
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- IRDB
- NDL
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用可