中性塩溶液におけるアルミニウムの腐食挙動に関する研究(第一報) : 中性塩溶液の還元特性について

DOI 機関リポジトリ Web Site

書誌事項

タイトル別名
  • On the corrosion of Aluminum immersed in neutral salt solution : Influence of anions on the cathodic reaction in neutral salt solution (part.1)
  • チュウセイエン ヨウエキ ニ オケル アルミニウム ノ フショク キョドウ ニ カンスル ケンキュウ 1

この論文をさがす

抄録

type:Article

The experiments to study the cathodic polarization character of neutral salt solution were carried out along the method of electrolysis under constant current. The following results were obtained. (1) The cathodic reaction on the corrosion of Aluminium is the reduction of dissolved oxygen and the reaction is proceed under the range of diffusion. Corrosion velocity is affected by the diffusion current. (2) The diffusion current density is more affected by the anions than the concentration of solution. (3) Thinking about, cathodic reaction and corrosion potential of Aluminium, cathodic reaction of Aluminium has no chance for nascent hydrogen reaction.

Alおよび，Al合金の腐食に関しては，これらの材料の使用条件からみて中性塩溶液における腐食挙動がもっとも重要だと考えられるが，これらの問題については従来，主として食塩溶液におげる分極特性や腐食と電位の報告がみられる程度でその腐食機構やイオン種の影響などに対する検討はかならずしも充分とは云えないようである。本報は中性塩溶液中におけるAlの腐食挙動を解明する一端として種々の中性塩溶液の還元特性ならびにそれらの溶液中のAlの腐食電位を測定した結果から，腐食のカソード反応ならびにアニオンの影響について検討したものである。

identifier:富山大学工学部紀要，15(1/2)