抄録

type:Article

In producing ferro-manganese we reduce Mn ore in electric furnace or high temperature blast furnace, the path of their chemical change of manganese oxide is not clearly known in raising the temperature. We tried to reduce them in the presence of CO or solid carbon in small muffle furnace from the temperature of 700℃ to 1500℃. And every 100℃ the sample were extracted and examined by X-ray. In these tests, the sample ores were pyrolusite (MnO_2) and contained small amount of braunite (MnO・3Mn_30_4・Si0_2) and Mn_30_4. Next results were known in reducing heating. At 700℃; Mn_20_3 and MnO appeared. At 800℃; No change. At 900℃; MnO increased， γ-Mn_20_3 appeared. At 1000℃; MnO a little increased. At 1100℃; Almost all structure w ere MnO, Mn_30_4 dicreased. At 1200℃; MnO increased. At 1300--1400℃; No change. At 1500℃; Mn_30_4 desappeared, MnO decreased and Fe-Mn solid solution appeared, but Mn carbides (Mn_3C, Mn_3C_4) were not formed.

マンガン鉱を高温電気炉又は高温高炉で還元してフエロマンガンを造る場合に，マンガン鉱の化学変化はただ想像されるだけで，それについて調べたものが無い。これらのことから著者らはインド産マンガン鉱を使ってCOガス又は炭素の存在下で鉱石を700℃から1500℃迄の間で加熱還元し，100℃毎にサンプルを取りX線で調べ，マンガン化合物の変化と金属マンガン，マンガン炭化物となる温度を調べた。又各種の化合物の生成について熱力学的にも考察を加へたが，マンガン炭化物については足掛りが出来た程度でなお深い研究を要する。これ等のことについての今迄の研究者はT.Yagi・hashi，K.Asada らで，COガスを使いマンガン鉱の還元挙動を解析している。著者らも昭和15年に，マンガン鉱石が各種の形のものがあることを示し，その製練法に言及している。

identifier:富山大学工学部紀要，24(1/2)

収録刊行物

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ