絹クレープの樹脂加工による品質改善に就いて

DOI HANDLE オープンアクセス

書誌事項

タイトル別名
  • On the improvements of silk crapes by the synthetic resin finishing

この論文をさがす

抄録

(1) Urea melamine formaldehyde and thiourea melamine formaldehyde resin sized fabrics are water repellented, so the crinkles of crapes were never swelled by water. The feeling of resin treated fabrics was rather slightly stiffy but the resilience, frictional strength and anti-shrinking were improved, (2) The sized fabrics were more durable in exposuring to the ultra-violet ray and had more tensile strength than the unsized ones, especially in the thiourea melamine formaldehyde resin, and it was also effective in anti-yellowing. (3) In Van Gieson's dyeing method the sized and the unsized showed different colourings.

(1) 絹クレープの樹脂加工によるシボ(Crinkles)の変化及び各種物理, 化学的効果に就いて研究した. (2) 樹脂加工区は防水性なる為に水分によるシボの変化は認められなく, 硬さは樹脂加工により僅に硬くなる. 然るに弾性度は10～20%の向上を認めた. 防縮効果に於ては経方向約2%, 緯方向2～5%の効果があつた. (3) 樹脂加工を施したものは強度に於て僅かに増加するも伸度は多少劣る. 紫外線による曝射に対しても何等変化を認めなく対照区に比して強度は大きい. 特にチオ尿素樹脂処理白布区に於て著るしい. 又同区は黄化防止にも効ある事を認めた.摩擦強度は何れも約45%向上した. (4) 染色性に就いては, 無処理布はすでに精練による熱処理を相当に受け, 好酸性(Oxyphil)に変化しVanGiesdn氏染法によ夢赤紫色に染るも, 樹脂処理区は黄色に染着し染色性を異にする.

収録刊行物

キーワード

詳細情報 詳細情報について

  • CRID
    1390853649767497984
  • NII論文ID
    110001456468
  • NII書誌ID
    AN0005519X
  • DOI
    10.15017/21218
  • HANDLE
    2324/21218
  • 本文言語コード
    ja
  • データソース種別
    • JaLC
    • IRDB
    • CiNii Articles

問題の指摘

ページトップへ