- Effect of Cold Rolling on the Creep Rupture Strength of 12Cr-5.4W Ferritic Steel with δ-ferrite
- dフェライト オ ユウスル 12Cr-5.4Wコウ ノ クリープハダンキョウド ニ オヨボス レイカン アツエン ノ エイキョウ
この論文をさがす
抄録
<p>This study examined cold rolling (20%) effects on the creep rupture strength of 12Cr-5.4W ferritic steel with martensite and δ-ferrite at 700 °C. Creep rupture strength of the as-received steel was equal to or greater than that of Gr.92 steel under 100-50 MPa, but cold rolling decreased the creep rupture strength by as much as 10%. Microstructure observations of crept steels revealed coarsening of the Laves phase by cold rolling in δ-ferrite but not in martensite. This finding suggests that the Laves phase coarsening in δ-ferrite is related to short-circuit diffusion because fine sub-grain structures were observed inside δ-ferrite grains in the cold-rolled steel after creep. Also, the martensite lath structure in the cold-rolled steel recovered quickly. Collectively, these cold-rolling-related phenomena of microstructural degradations are inferred as factors decreasing the creep rupture strength. In the as-received steel, some creep voids were observed in martensite: most were observed adjacent to coarse vanadium nitrides. By contrast, creep voids in the cold-rolled steel were most numerous near the martensite – δ-ferrite interface. It was suggested that nucleation of creep voids near the interface in the cold-rolled steel was attributed to mechanisms such as the Laves phase size and distribution at the interface and stress concentration effects of dislocations that were piled up toward the interface.</p>
収録刊行物
-
- 鉄と鋼
-
鉄と鋼 108 (2), 131-140, 2022
一般社団法人 日本鉄鋼協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390853879745765760
-
- NII論文ID
- 130008149093
-
- NII書誌ID
- AN00151251
-
- ISSN
- 18832954
- 00211575
-
- NDL書誌ID
- 031952675
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可