- 林 主愛
- Department of Science and Technology, Graduate School of Engineering, Nagasaki University
-
- 田畑 直哉
- Department of Advanced Engineering, Graduate School of Engineering, Nagasaki University
-
- 佐々野 創
- Department of Advanced Engineering, Graduate School of Engineering, Nagasaki University
-
- 村上 裕人
- Division of Materials Science, Graduate School of Engineering, Nagasaki University
書誌事項
- タイトル別名
-
- Synthesis and Properties of Polyurethane Crosslinked by Polyrotaxane Consisting of Monoaminocyclodextrin
説明
<p>A polyurethane (PU) crosslinked by a polyrotaxane (PRX), which consists of monoamino-α-cyclodextrin(amCyD) and poly(ethylene glycol)4000 (PEG4000), was designed to decrease the formation of multiple crosslinks from one CyD. The capping reaction of the pseudo-PRX containing amCyD was achieved by a click reaction. The filling ratio of amCyD in the PRX was ca. 74%. The PU crosslinked by the PRX(PU-PRXam(74)) was prepared by a prepolymer method. The thermal and physical properties of PU-PRXam(74) were compared with those of the PUs crosslinked by PRXs consisting of half-methylated CyD(PU-PRXMe(43) and PU-PRXMe(63)). The degree of swelling of PU-PRX-am(74) was ca. 1.3 times larger than those of PU-PRXMes, suggesting the decrease in the multiple crosslinks from one CyD. The DSC and dynamic viscoelastic measurements revealed that PU-PRXam(74) shows a unique relaxation after its glass transition. In the tensile test results, PU-PRXam(74) showed the best elongation among the PU-PRXs whereas the tensile strength was lower than the others. This result is also evidence of the decrease in the multiple crosslinks from one CyD.</p>
収録刊行物
-
- 日本ゴム協会誌
-
日本ゴム協会誌 95 (1), 1-7, 2022