Effect of Reinforcing Steel Fiber on Permeability of High Strength and Ultra-Low Permeability Concrete
-
- Sakemoto Kotone
- Graduate School of Engineering, Hokkaido University
-
- Kato Masaji
- Faculty of Engineering, Hokkaido University
-
- Ishii Yusuke
- Central Research Lab., Taiheiyo Cement Corporation
-
- Kurumisawa Kiyofumi
- Faculty of Engineering, Hokkaido University
-
- Nara Yoshitaka
- Graduate School of Engineering, Kyoto University
この論文をさがす
抄録
<p>Information on the water permeability of materials for radioactive waste disposal in geological repositories is essential. High strength and ultra-low permeability concrete (HSULPC) is being considered as a material used to package transuranic (TRU) waste. HSULPC would be reinforced by steel fiber to increase its tensile strength and toughness, but the effect of reinforcing steel fiber on permeability is unclear. Permeability tests need to be highly accurate to determine the hydraulic properties of low permeability materials. In this study, the hydraulic conductivity of HSULPC with steel fiber using the transient pulse method. The hydraulic conductivities of HSULPC with/without steel fiber were determined to be around 10−13 to 10−11 m/s under the confining pressures between 2 and 10 MPa and pore pressure of 1 MPa constant. The results further showed that the permeability of these materials had a hysteretic dependence on the effective confining pressure. There was no remarkable difference of hydraulic conductivity between HSULPC with and without steel fiber. SEM observation revealed that HSULPC with steel fiber has isolated voids to some extent included during mixing of concrete but there are few voids on the interface of steel fiber for water channel. However, due to the higher porosity, the hydraulic conductivity of HSULPC with steel fiber is relatively higher than that without fiber. Still, the permeability of fiber reinforced HSULPC is low enough compared with Horonobe mudstone and Toki granite and would enable it to effectively confine 14C radionuclides in TRU waste.</p><p> </p><p>This Paper was Originally Published in Japanese in J. Soc. Mater. Sci., Japan 71 (2022) 228–234.</p>
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 63 (12), 1639-1644, 2022-12-01
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390857158422467328
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 032534832
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可