Activity of Chromium Oxide in Calcium Silicate Bearing Molten Slag for Highly Clean Chromium Steel Refining Process

DOI Web Site 被引用文献1件 参考文献26件
  • Liu Yuxing
    Department of Materials Science and Engineering, Tokyo Institute of Technology
  • Li Zhi
    Department of Materials Science and Engineering, Tokyo Institute of Technology
  • Kobayashi Yoshinao
    Laboratory for Zero-Carbon Energy, Institute of Innovative Research, Tokyo Institute of Technology

抄録

<p>Thermodynamic properties of chromium oxide in molten slags are essential to optimizing stainless steel refining processes and reduction processes of chromium ores. The present study conducts chemical equilibrium experiments at 1823 K (1550°C) under different oxygen partial pressures in order to investigate chromium oxide activity coefficient in CaO–CaF2–MgO–Al2O3–SiO2–MnO–CrOx slags with low chromium content taking the effect of MgO addition into consideration. An increase in MgO initial content from 0 to 20 mass% increases the activity coefficient of CrOx under the oxygen partial pressures of 6.38×10−12 atm and 1.60×10−10 atm. It is found that lower oxygen partial pressure may reduce solid phase formation. The present study recommends the usage of 29 mass% CaO-5 mass% CaF2-20 mass% MgO-10 mass% Al2O3-29 mass% SiO2-5 mass% MnO-2 mass% Cr2O3 slag to reduce chromium loss at 1823 K (1550°C) under the oxygen partial pressure of 6.38×10−12 atm, where the activity coefficient of CrOx is the highest in the slags without solid phase.</p>

収録刊行物

被引用文献 (1)*注記

もっと見る

参考文献 (26)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ