Deformation by Slip Along One System of Crystallographic Planes of Potassium Bromide Single Crystals.

DOI 機関リポジトリ Web Site

書誌事項

タイトル別名
  • シュウカ カリウム タンケッショウ ノ タンイツスベリ ヘンケイ エイブン
  • 臭化カリウム単結晶の単一すべり変形

この論文をさがす

抄録

type:Article

To obtain basic information about the strain hardening phenomenon in crystals a specially designed device was newly produced. By making use of this device dislocation movement along one glide system od crystallographic planes<110>in KBr single crystal was studied through the observation of dislocation etch pit figures. A comparison the deformation by slip along one system with that from uniaxial compression test along<100>axis was done. It was found that the strain herdening in the course of the deformation by slip along one system was markedly supressed as well as that the region of the easy glide (stage I) was expanded up to about 4 per cent strain. The applicabilities of the present device are discussed by comparing with various methods proposed by other investigators so far.

歪硬化現象に関する基礎的知見を得るため,単一すべり変形装置の作製を行った。本装置を用いて臭化カリウム単結晶の結晶方位〈110〉に沿った単一すべり変形を行った。変形に伴う転位の挙動を調べるためにその腐食像の観察を行った。その結果,〈110〉方位の単一すべり変形時に観測される歪硬化係数は,〈110〉方位の一軸圧縮変形時のそれよりも顕著に減少すること及び容易すべり領域が約4%歪まで拡張されることが明らかになった。さらに,他の研究者により提案されている単一すべり変形法と本装置との比較を行うとともに本装置の応用について検討を行う。

収録刊行物

詳細情報 詳細情報について

問題の指摘

ページトップへ