High-Pressure Synthesis and Magnetic Property of a Novel Ferrimagnetic Quadruple Perovskite YMn₃Co₄O₁₂
-
- Tanaka Atsushi
- Department of Materials Science, Graduate School of Engineering, Osaka Prefecture University
-
- Yamada Ikuya
- Department of Materials Science, Graduate School of Engineering, Osaka Prefecture University
-
- Kawaguchi Shogo
- Japan Synchrotron Radiation Research Institute (JASRI)
書誌事項
- タイトル別名
-
- High-Pressure Synthesis and Magnetic Property of a Novel Ferrimagnetic Quadruple Perovskite YMn<sub>3</sub>Co<sub>4</sub>O<sub>12</sub>
この論文をさがす
抄録
<p>A novel quadruple perovskite oxide YMn3Co4O12 has been synthesized in high-pressure and high-temperature conditions of 16 GPa and 1473 K, respectively. Rietveld refinement of synchrotron X-ray powder diffraction data reveals that this oxide crystallizes in a cubic quadruple perovskite structure in a space group of Im3 (No. 204) with a 1:3-type atomic ordering of Y and Mn at A-sites, and the bond valence analysis suggests the valence state of YMn3+3Co3+4O12. A ferromagnetic-like transition is observed at ∼125 K and the magnetization value reaches up to ∼3 μB per formula unit at 5 K. The low-temperature magnetic state can be interpreted as ferrimagnetism with antiparallel alignment of A′-site Mn3+ (S = 2) and B-site Co3+ (high-spin, S = 2), which is in contrast to the antiferromagnetism in other A′-Mn-containing quadruple perovskite oxides. This finding proposes that the coexistence of A′-Mn3+ and B-Co3+ leading to ferrimagnetic state is realized in the specific structure with distinct crystallographic sites.</p>
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 64 (9), 2105-2108, 2023-09-01
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390860177971202176
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 033026451
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- KAKEN
-
- 抄録ライセンスフラグ
- 使用不可