Effect of ultraviolet irradiation treatment on shear bond strength between polymethyl methacrylate and cobalt-chromium-molybdenum alloy
-
- THANT San Win
- Advanced Prosthodontics, Oral Health Sciences, Graduate School of Medical and Dental Sciences, Tokyo Medical and Dental University
-
- TAKAICHI Atsushi
- Advanced Prosthodontics, Oral Health Sciences, Graduate School of Medical and Dental Sciences, Tokyo Medical and Dental University
-
- KAJIMA Yuka
- Advanced Prosthodontics, Oral Health Sciences, Graduate School of Medical and Dental Sciences, Tokyo Medical and Dental University
-
- MOHAMED Amr
- Advanced Prosthodontics, Oral Health Sciences, Graduate School of Medical and Dental Sciences, Tokyo Medical and Dental University
-
- NOZAKI Kosuke
- Advanced Prosthodontics, Oral Health Sciences, Graduate School of Medical and Dental Sciences, Tokyo Medical and Dental University
-
- TAKAHASHI Hidekazu
- Course for Oral Health Engineering, Faculty of Dentistry, Tokyo Medical and Dental University
-
- CHEN Peng
- Metallic Biomaterials, Biomedical Materials, Institute of Biomaterials and Bioengineering, Tokyo Medical and Dental University
-
- HANAWA Takao
- Metallic Biomaterials, Biomedical Materials, Institute of Biomaterials and Bioengineering, Tokyo Medical and Dental University
-
- WAKABAYASHI Noriyuki
- Advanced Prosthodontics, Oral Health Sciences, Graduate School of Medical and Dental Sciences, Tokyo Medical and Dental University
抄録
<p>We aimed to elucidate the effects of ultraviolet (UV) irradiation on the shear bond strength (SBS) between heat-cured polymethyl methacrylate (PMMA) and a Co-Cr-Mo alloy. Disk-shaped Co-Cr-Mo alloy prepared by casting were subjected to different UV treatment times (0, 15, and 30 min). To determine the effect of UV treatment on surface properties of the alloy, surface roughness, wettability, and chemical compositions were analyzed. To evaluate the SBS, cylindrical PMMA was bonded to the UV-treated alloy, and subsequently subjected to the SBS test after 24 h of storage at room temperature or following 10,000 thermal cycles (n=10/group). After the UV treatment, the surface roughness remained unchanged, but oxidation resulted in the surface exhibiting greater hydrophilic characteristics. The UV-treated group showed significantly higher SBS values than those of the non-treated group (p<0.001). These results suggested that UV treatment-mediated oxidation improved the bond strength between PMMA and Co-Cr-Mo alloy.</p>
収録刊行物
-
- Dental Materials Journal
-
Dental Materials Journal 42 (5), 748-755, 2023-09-25
一般社団法人 日本歯科理工学会