In Situ Residual Stress Analysis in a Glass Fiber-reinforced Phenolic Resin Having a Fiber Orientation and Copper Composite Material During Curing
-
- KAKARA Takeshi
- Corporate Engineering Center, Sumitomo Bakelite Co., Ltd. Corporate Engineering Center, Sumitomo Bakelite Co., Ltd. Japan Synchrotron Radiation Research Institute
Bibliographic Information
- Other Title
-
- 繊維配向を有するガラス繊維強化フェノール樹脂/ 銅複合材の熱硬 化過程における樹脂/ 銅界面の残留応力その場観察
Abstract
<p>Residual stress at the interface between a glass fiber-reinforced phenolic resin having a fiber orientation and copper foil was analyzed in situ during curing and thermal-testing via time-resolved X-ray diffraction measurements using a sin 2 Ψ method, in which the specimen was prepared via a transfer molding. The residual stress, which was estimated from the stress in copper, shifted toward tensile and compressive stress directions in heating and cooling, respectively, due to a difference in the magnitude of thermal expansion and contraction between the resin and copper. There was an anisotropy of coefficient of linear expansion( CTE) of the resin due to the fiber orientation, which caused a residual stress anisotropy. The temperature at a stress-free state indicated that the residual stress was also affected by a resin temperature at which the resin-copper adhesive interface first formed during molding.</p>
Journal
-
- Journal of The Adhesion Society of Japan
-
Journal of The Adhesion Society of Japan 57 (2), 51-57, 2021-02-01
The Adhesion Society of Japan
- Tweet
Keywords
Details 詳細情報について
-
- CRID
- 1390861383231510912
-
- ISSN
- 21874816
- 09164812
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- Crossref
-
- Abstract License Flag
- Disallowed