Precipitation Behavior of M<sub>23</sub>C<sub>6</sub> and Fe<sub>2</sub>W in 9Cr3W3CoVNbBN Steel during Tempering in the Temperature Range of 500–790°C
-
- Osanai Takumi
- Graduate School of Engineering, Tohoku University Steel Research Laboratories, Nippon Steel Corporation
-
- Sekido Nobuaki
- Graduate School of Engineering, Tohoku University
-
- Yonemura Mitsuharu
- Advanced Technology Research Laboratories, Nippon Steel Corporation
-
- Maruyama Kouichi
- Professor Emeritus, Tohoku University
-
- Yoshimi Kyosuke
- Graduate School of Engineering, Tohoku University
抄録
<p>The precipitation behavior of M23C6 and Fe2W was investigated in a boron-doped 9%Cr-3%W-3%Co steel during tempering at temperatures from 500 to 790°C. During tempering at high temperatures, M23C6 precipitation occurred earlier than Fe2W, but this precipitation sequence was reversed below 550°C. The Fe2W precipitates formed on PAGBs during tempering at the lower temperatures showed a continuous film morphology. The film-shaped Fe2W precipitates were stable after aging for at least 100 h at 650°C.</p>
収録刊行物
-
- ISIJ International
-
ISIJ International 64 (2), 286-294, 2024-01-30
一般社団法人 日本鉄鋼協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390861925380463360
-
- ISSN
- 13475460
- 09151559
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- Crossref
-
- 抄録ライセンスフラグ
- 使用不可