- High Corrosion Resistance Zinc-Nickel-SiO<sub>2</sub> Composite Plating with Excellent Hydrogen Embrittlement Properties
抄録
<p>The investigation of the film structure and hydrogen embrittlement resistance of Zn-Ni-SiO2 composite plating film and Ti-Cd plating film with excellent hydrogen embrittlement resistance demonstrated that the Zn-Ni-SiO2 composite plating film plated from acidic chloride bath had equal hydrogen permeability to that of the Ti-Cd plating film. Furthermore, cross-sectional observation revealed the structure of Zn-Ni-SiO2 composite plating film. This crack structure presumably supports the high hydrogen permeability and the porous structure of Ti-Cd plating film.</p> <p>These findings suggest that the Zn-Ni-SiO2 composite plating film from an acid chloride bath has high functionality and effectiveness for application to high-strength components. This paper introduces the structure and hydrogen embrittlement resistance properties of this composite coating.</p>
収録刊行物
-
- 表面技術
-
表面技術 75 (2), 97-101, 2024-02-01
一般社団法人 表面技術協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390862036412728832
-
- ISSN
- 18843409
- 09151869
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
-
- 抄録ライセンスフラグ
- 使用不可