Effect of Carburizing Atmosphere on High-Temperature Oxidation Resistance of 17% Cr Ferritic Stainless Steel Doped with Cu and Ni
-
- Hayashi Atsutaka
- Research & Development Center, NIPPON STEEL Stainless Steel Corporation
-
- Hiraide Nobuhiko
- Research & Development Center, NIPPON STEEL Stainless Steel Corporation
-
- Hamada Jun-ichi
- Research & Development Center, NIPPON STEEL Stainless Steel Corporation
-
- Inoue Yoshiharu
- Products Development Division, NIPPON STEEL Stainless Steel Corporation
Bibliographic Information
- Other Title
-
- 17%Cr添加フェライト系ステンレス鋼の耐酸化性に及ぼすCu,Ni添加および浸炭性雰囲気の影響
Abstract
<p>Stainless steel is used as a heat-resistant material not only in air, but also in carburizing atmospheres containing CO and CO2. Carburization may cause austenization for ferritic stainless steels. In this study, the high-temperature oxidation behaviors of 17% Cr ferritic stainless steels with and without the addition of austenite-forming elements, such as Cu and Ni, in a carburizing atmosphere at 1123 K were investigated. The steels did not exhibit breakaway oxidation in the temperature range of 1123-1273 K in air. However, doping the steels with Cu and Ni enhanced breakaway oxidation in a carburizing atmosphere at 1123 K. Traces of austenization and carburization were observed at the base metal under the breakaway oxidation scale of the 17% Cr steel doped with 1% Cu and 1% Ni. Thus, it is proposed that the breakaway oxidation of the ferritic stainless steels in a carburizing atmosphere is attributed to austenization induced by carburization and doping with austenite-forming elements.</p>
Journal
-
- Journal of the Japan Institute of Metals and Materials
-
Journal of the Japan Institute of Metals and Materials 88 (4), 81-89, 2024-04-01
The Japan Institute of Metals and Materials
- Tweet
Details 詳細情報について
-
- CRID
- 1390862545803770240
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- Crossref
-
- Abstract License Flag
- Disallowed