- High-Temperature Corrosion of Refractories in Simulated lncinerator Ash under Hydrogen Chloride Gas
- エンカ スイソ フンイキ カ デ ノ ショウキャクロ モギ ハイ ニ ヨル タイカブツ ノ コウオン フショク
この論文をさがす
説明
Using the crucible method，laboratory corrosion test on refractories was conducted in a simulated incinerator ash under dry or wet 1．86％HCl gas at1000℃． In the case of corrosion test in ash，glass phase of Na－K－Si-O system was formed in the sample surface，and the mass of sample increased after corrosion test． Basic oxides included in the ash and the refractories changed the chloride under HCl gas．Since the formed chloride volatilized，the glass formation was inhibited．When there was no ash，the basic oxides included in grain boundary of the refractories volatilized，and embrittlement was generated．
収録刊行物
-
- 耐火物
-
耐火物 54 (5), 249-251, 2002-05-01
耐火物技術協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390863329503929984
-
- NII論文ID
- 10008201151
-
- NII書誌ID
- AN00136247
-
- ISSN
- 27593835
- 00398993
-
- NDL書誌ID
- 6152124
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDLサーチ
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可