Compressive Strength and Thermal Properties of Ferro Coke Prepared by Cold Pressing Method

DOI Web Site 18 References
  • Li Yanhui
    College of Chemical Engineering, North China University of Science and Technology
  • Liao Fei
    College of Chemical Engineering, North China University of Science and Technology
  • Guo Rui
    College of Chemical Engineering, North China University of Science and Technology
  • Cheng Huan
    College of Chemical Engineering, North China University of Science and Technology
  • Sun Zhang
    College of Chemical Engineering, North China University of Science and Technology
  • Gao Zhennan
    Kailuan Energy Chemical Co, LTD
  • Hao Liangyuan
    HBIS Group Co, LTD

Search this article

Description

<p>This research aimed to investigate the production of ferro coke with high strength by cold pressing without adding binder, to meet the requirements of the metallurgical industry and avoid the environmental pollution problems caused by the hot pressing process. The effects of pressure and proportion of iron ore powder on the preparation of ferro coke from a weakly caking coal and a strongly caking coal were studied. The results show that when no binder is added, the ferro coke made from weakly caking coal has the highest compressive strength of 5.13 KN, while the ferro coke made from strongly caking coal has the highest compressive strength of 4.93 KN.</p><p>The relationship between the strength of ferro coke and the rate of dissolution loss was studied, and it was found that weakly caking coal produced under high forming pressure had good performance.</p>

Journal

  • ISIJ International

    ISIJ International 64 (14), 1999-2007, 2024-12-15

    The Iron and Steel Institute of Japan