- Ogawa Masato
- Department of materials, Kyushu University
-
- Sumita Takehiro
- Department of materials, Kyushu University
-
- Saito Noritaka
- Department of materials, Kyushu University
-
- Nakashima Kunihiko
- Department of materials, Kyushu University
-
- Shimamura Yuta
- Steelmaking Process Group, Process Development Office, Research & Development Center, Sanyo Special Steel Co., Ltd.
-
- Yoshioka Takanori
- Steelmaking Process Group, Process Development Office, Research & Development Center, Sanyo Special Steel Co., Ltd.
この論文をさがす
説明
<p>Wettability between molten iron and non-metallic inclusions is an important factor, as it influences the behavior of non-metallic inclusions during secondary metallurgy. In the present study, the wettability of CaS against molten iron was investigated using the sessile drop method at 1873 K. The CaS substrate was fabricated using spark plasma sintering, achieving a high relative density of 98%. The measured contact angle of CaS against molten iron was found to be 118 degrees. This finding indicates that the wettability of CaS is poor, which contrasts with the previous report. This result will contribute to further understanding regarding the inclusions’ behavior during secondary refining processes.</p>
収録刊行物
-
- ＩＳＩＪ Ｉｎｔｅｒｎａｔｉｏｎａｌ
-
ＩＳＩＪ Ｉｎｔｅｒｎａｔｉｏｎａｌ 65 (2), 323-325, 2025-02-15