- Effects of Rolling Temperature and Annealing Temperature on Mechanical Properties of Mg–8％Al–1％Zn–1％Ca Alloy Medium Plates
- Mg-8%Al-1%Zn-1%Ca ゴウキン チュウ イタザイ ノ キカイテキ トクセイ ニ オヨボス アツエン オンド オヨビ ショウドン オンド ノ エイキョウ
この論文をさがす
抄録
<p>The mechanical properties and microstructure of rolled and annealed Mg–8 mass％Al–1 mass％Zn–1 mass％Ca (AZX811) alloy plates were investigated. To investigate the effect of rolling temperature, samples were prepared by rolling at 623 K and 723 K, following which annealing was performed at 473 K. The size of the Al–Ca compound was finer in the 723 K rolled sample than in the 623 K rolled sample. The higher tensile strength and elongation of the 723 K rolled sample compared to the 623 K rolled sample were attributed to the finer Al–Ca compounds in the former. In addition, the effect of annealing temperature on the mechanical properties and microstructure of the 723 K rolled AZX811 alloys were investigated. As a result of these investigations, a decrease in proof stress and an increase in failure elongation were observed when the annealing temperature was set to 573 K. This was mainly ascribed to a decrease in the fraction of grains below 10 µm in size, a decrease in the basal texture intensity, and a solid solution of fine Mg17Al12 precipitates.</p>
収録刊行物
-
- 日本金属学会誌
-
日本金属学会誌 84 (12), 391-398, 2020-12-01
公益社団法人 日本金属学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1391412326419458432
-
- NII論文ID
- 130007942359
-
- NII書誌ID
- AN00187860
-
- ISSN
- 18806880
- 24337501
- 00214876
-
- NDL書誌ID
- 030803644
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可