Formation of a Diffusion Barrier Coating on Ni-Based Alloy and Thermal Cycle Oxidation Property
-
- Saito Shigeru
- Laboratory of Advanced Materials for Cold Region, Hokkaido University of Science
-
- Hayashi Shigenari
- Faculty of Engineering, Hokkaido University
-
- Narita Takuro
- DBC System R and D Co., Ltd.
-
- Kato Yasumichi
- DBC System R and D Co., Ltd.
-
- Ohtsuka Motohiro
- DBC System R and D Co., Ltd.
-
- Ara Mayumi
- DBC System R and D Co., Ltd.
-
- Narita Toshio
- DBC System R and D Co., Ltd.
この論文をさがす
説明
<p>A diffusion-barrier coating layer (DBC) was formed on a Ni–22Cr–19Fe–9Mo alloy by Al-pack cementation at 1000°C followed by heat treatment at 1100°C. The thermal cyclic oxidation behavior of the DBC system was then investigated. The thermal cycle oxidation tests were conducted at 1100°C in air for 45 min, each followed by 15 min at room temperature. Electron probe micro-analysis (EPMA) was performed to determine the microstructure and concentration profile of each element between the substrate and the coating layer.</p><p>The DBC system showed good thermal cycle oxidation property. The layer structure between the substrate and the coating layer after thermal oxidation cycling is discussed with respect to the composition paths plotted in the Ni–Cr–Fe and Ni–Cr–Al phase diagrams. The coating layer structure after 100 cycles of 45 min at 1100°C consisted of the γ- and α-phases of the Ni–Cr–Fe system and the β-phase of the Ni–Cr–Al system. The coating layer structure after 400 cycles of 45 min at 1100°C consisted of the γ-phase of the Ni–Cr–Fe system and the β-phase of the Ni–Cr–Al system. In contrast, the coating layer structure after 900 cycles of 45 min at 1100°C consisted of the γ-phase of the Ni–Cr–Fe system.</p><p> </p><p>This Paper was Originally Published in J. Japan Inst. Met. Mater. 83 (2019) 372–377.</p>
収録刊行物
-
- MATERIALS TRANSACTIONS
-
MATERIALS TRANSACTIONS 61 (12), 2336-2341, 2020-12-01
公益社団法人 日本金属学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1391693801396759808
-
- NII論文ID
- 130007942353
-
- NII書誌ID
- AA1151294X
-
- ISSN
- 13475320
- 13459678
-
- NDL書誌ID
- 030779606
-
- 本文言語コード
- en
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可