<i>R</i>型六方晶フェライト構造を有する酸化物BaFe<sub><i>x</i></sub>Co<sub>6-<i>x</i></sub>O<sub>11</sub>（0 ≦ <i>x</i> ≦ 4）の高圧合成と物性評価
書誌事項
- タイトル別名
-
- High Pressure Synthesis and Physical Property Measurements of <i>R</i>-type Hexagonal Ferrite-Structure Oxides BaFe<sub><i>x</i></sub>Co<sub>6-<i>x</i></sub>O<sub>11</sub> (0 ≦ <i>x</i> ≦ 4)
- R型六方晶フェライト構造を有する酸化物BaFe[x]Co[6-x]O₁₁(0≦x≦4)の高圧合成と物性評価
- Rガタ ロッポウショウフェライト コウゾウ オ ユウスル サンカブツ BaFe[x]Co[6-x]O ₁ ₁(0 ≦ x ≦ 4)ノ コウアツ ゴウセイ ト ブッセイ ヒョウカ
この論文をさがす
説明
<p>Single phase samples of a cobaltite BaCo6O11 and its Fe-substituted derivatives BaFexCo6-xO11, which have R-type hexagonal ferrite structures, were successfully synthesized by a high-pressure and high-temperature method. BaCo6O11 was found to be a ferromagnetic metal. Mixed valent Co3.4+ cations at the octahedral B(1) and B(2) sites contribute to the metallic conduction, whereas Co3+ cations at the trigonal-bipyramidal B(3) site give local magnetic moments, which order ferromagnetically below the Curie temperature of 17 K. The Fe substitution largely increases the magnetic transition temperature and changes the ground state to a ferrimagnetic semiconductor owing to the introduction of localized Fe3+ cations at the B(1) and B(2) sites.</p>
収録刊行物
-
- 粉体および粉末冶金
-
粉体および粉末冶金 67 (12), 675-681, 2020-12-15
一般社団法人 粉体粉末冶金協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1391975831219950592
-
- NII論文ID
- 130007955814
-
- NII書誌ID
- AN00222724
-
- ISSN
- 18809014
- 05328799
-
- NDL書誌ID
- 031200524
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDLサーチ
- Crossref
- CiNii Articles
- OpenAIRE
-
- 抄録ライセンスフラグ
- 使用不可