- Change in Mechanical Properties of Oxide Ceramics by Heat Treatment under Vacuum Condition
- シンクウ ネツ ショリ ニ ヨル サンカブツ セラミックス ノ キカイテキ セイシツ ノ ヘンカ
この論文をさがす
抄録
iAlumina and Y203-partially stabilized zirconia(PSZ) which were typical oxide ceramics were heat-treated in vacuum in holding time of 3h and the temperatures between 1300℃ and 1600℃. All test pieces showed mass loss by the heat-treatment.The amount of mass loss of the alumina was more abounding than that of the Y203-PSZ.Though the mass loss seemed to be due to vaporization from the sample surface,vapor species did not be identified.Bending strength of alumina and Y203-PSZ did not show the remarkable change by heat treatment up to 1500℃,but decreased suddenly at 1600℃.It is considered that one of the factors of strength degradation is the grain growth by heat-treatment.In case of the alumina,Vickers hardness showed the decrease of about 10% up to1500℃ and the decrease of about 30% at l600℃. In case of the Y203-PSZ,Vickers hardness showed the decrease of about 10%i n all tested temperature range.The degree of degradation of measured physical property of the Y203 PSZ was smaller than that of the alumina. The Y203-PSZ was more stable than the alumina for heat treatment.
収録刊行物
-
- 耐火物
-
耐火物 54 (6), 286-291, 2002-06-01
耐火物技術協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390581854527219456
-
- NII論文ID
- 10008646365
-
- NII書誌ID
- AN00136247
-
- ISSN
- 27593835
- 00398993
-
- NDL書誌ID
- 6177022
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可