Time-resolved microphotoluminescence study of Cu(In,Ga)Se2

DOI Web Site Web Site Web Site 1 Citations 29 References

Bibliographic Information

Other Title
  • Time resolved microphotoluminescence study of Cu In Ga Se2
  • Special issue: Ternary and multinary compounds
  • Special issue Ternary and multinary compounds

Search this article

Abstract

<jats:p> The carrier recombination processes in Cu(In<jats:sub>1-<jats:italic>x</jats:italic> </jats:sub>,Ga<jats:sub> <jats:italic>x</jats:italic> </jats:sub>)Se<jats:sub>2</jats:sub> (CIGS) thin films were investigated by time-resolved microscopic-photoluminescence (µ-PL) measurement at room temperature. For films with <jats:italic>x</jats:italic> = 0.45, the spatial distribution of the donor–acceptor pair luminescence is much larger than the grain size. The PL decay lifetime is directly correlated with the µ-PL intensity, but the spectral shape is identical regardless of the sample position. These results suggest that the nonuniform distribution of nonradiative recombination centers mainly affects the carrier recombination in CIGS thin films. At relatively high Ga concentrations (<jats:italic>x</jats:italic> ≥0.7), the spatial inhomogeneity in µ-PL intensity is enhanced and decay accelerated, suggesting an increase in the density of nonradiative recombination centers. Thus, suppression of nonradiative recombination is critical to enhancing the performance of CIGS-based solar cells. </jats:p>

Journal

Citations (1)*help

See more

References(29)*help

See more

Related Projects

See more

Keywords

Details 詳細情報について

Report a problem

Back to top