Mechanical Properties on Electron Beam Welds of Constructional High Tension Steels (Report IV)

この論文をさがす

抄録

The effects of bead width and hardness difference between the electron-beam weld and the base metal on the transition temperature for fracture mode (Trm) in Charpy impact ductility test were studied in this investigation by using HT50 and 80 constructional high tensile steels. The remarkable conclusion are as follows: (1) The impact strength of the weld metal is not depended on the variation of a_b parameter. (2) Moreover with an increase of weld heat input or notch depth for Charpy test specimen, the Trm tends to be raised. (3) With an increase of the annealing temperature, the T_<rm> tends to be raised in general. (4) The impact strength for HT50 and 80 weld metals was not depended on the variation of the hardness of the weld metal except for the HT50 weld with 650℃ annealing. (5) The T_<rm> tends to be raised with an increase of bead width ratio, or with a decrease of hardness difference ratio. (6) Isothermal lines for the T_<rm> more than 100℃ were made clear by the two parameters of the bead width ratio and the hardness difference ratio.

収録刊行物

詳細情報

  • CRID
    1570291227348563840
  • NII論文ID
    110006484532
  • NII書誌ID
    AA00867058
  • ISSN
    03874508
  • 本文言語コード
    en
  • データソース種別
    • CiNii Articles

問題の指摘

ページトップへ