Neutron Diffraction Study on Preferred Orientation of Ag-Sheathed Y–Ba–Cu–O Superconductor Tape with <I>J</I><SUB>c</SUB>=1000–3000 A/cm<SUP>2</SUP>

Search this article

Description

Ag-sheathed tapes using tetragonal phase of YBa2Cu3Ox were fabricated by cold rolling. Neutron diffraction study was undertaken to investigate the orientation of YBCO grains in the Ag-sheathed tape. It was clearly observed that the c-plane of crystal was aligned parallel to the cold rolling surface with a standard deviation of 26.7 degree. The preferred orientation was enhanced by using the tetragonal phase.