Structure and Stability of a Splat-Cooled Fe-P-C Alloy

機関リポジトリ

この論文をさがす

説明

The structure and the stability of a splat-cooled iron-based alloy (80Fe-13P-7C) were investigated by using electron and X-ray diffraction methods, high voltage electron microscopy and field ion microscopy. No appreciable change occurred in the transmission electron diffraction pattern as well as in the transmission electron microscope image by the irradiation of electrons being accelerated at any voltage in the range of 100 kV-1000 kV up to the total dose of 10^<23> electrons/cm^2. However, when the specimen was heated in-situ up to 200℃ under irradiation, the splitting of the second halo ring disappeared already at the total dose of 2×10^<22> electrons/cm^2, whereas such change did not occur in the unirradiated region of the specimen. Furthermore, crystallization was retarded in the irradiated region. Pole figure determination indicates no development of preferred orientation in the crystallization process of the splat-cooled alloy and also the cold rolled sheet of the alloy. The field ion micrographs obtained with the splat-cooled alloy tips were far different from the imaging ring patterns which were observed with the crystallized one and the data which support positively the existence of the microcrystalline phase have not been obtained so far (color superposition method is now being applied). The observations by dark field electron microscopy and lattice fringe electron microscopy made in parallel to FIM observation so far support the FIM observation.

収録刊行物

詳細情報 詳細情報について

問題の指摘

ページトップへ