真空圧延接合装置の試作とクラッド材の製造 : 真空圧延接合法によるクラッド材の製造とその特性(第1報)(平成3年度春季全国大会論文発表講演論文)

被引用文献21件

書誌事項

タイトル別名
  • Development of Vacuum Roll Bonding Apparatus and Production of Clad Metals-Development of Clad Metals by Vacuum Roll Bonding and its Characteristics (Report 1)-

この論文をさがす

説明

A vacuum roll bonding apparatus has been developed to produce clad metals. Clad metals such as Al/SS41,A5083/SS41,Cu/SS41,Ti/SS41,SUS304/SS41,Al/Cu, Al/Ti, Cu/Ni, Cu/Ti and Nb/Ti were produced at temperature in the range 0.7-0.85 of the homologous melting temperature using the vacuum roll bonding. And bond mechanism on this method, bond microstructure and bond strength of the clad metals have been investigated. The results obtained are as follows ;(1) Bondings of dissimilar metals such as aluminum clad steel, which is difficult to bond by diffusion bonding, were performed under the low reduction in thickness.(2) Though the bondings were performed at elevated temperature, interdiffusion of the elements at the bond interface which occurred during the bonding and cooling process was so little that it was not detected by EPMA analysis.(3) Bond shear strength of A5083/SS41,SUS304/SS41 and Ti/SS41 was higher than that specified by JIS. As the bond shear strength of other clad metals was very high, shear fracture at the bond interfaces did not develop on the shear test.

収録刊行物

被引用文献 (21)*注記

もっと見る

キーワード

詳細情報 詳細情報について

  • CRID
    1574231877113885440
  • NII論文ID
    110003423664
  • NII書誌ID
    AN1005067X
  • ISSN
    02884771
  • 本文言語コード
    ja
  • データソース種別
    • CiNii Articles

問題の指摘

ページトップへ