Ion-assisted coating for large-scale Bimorph deformable mirror
この論文をさがす
説明
We have fabricated a 410 x 468 mm size deformable mirror with 100 Bimorph piezoceramic actuators for the LFEX laser system at Osaka University. In the case of Bimorph-type deformable mirrors, the mirror surface had to be polished and coated after bonding the piezoceramic actuators to the rear side of the thin mirror substrate. This provides a good surface figure, but the coating temperature for the high-reflection mirror was strictly limited because of the thermal fragility of piezoceramic actuators. The mirror substrate with the actuators was polished, and an ion-assisted multilayer dielectric coating was produced at 60 degrees Celsius with our 80-inch coating chamber. The flatness of the mirror just after coating was 7 μm, and reduced by aging to 3.2 μm when the mirror was assembled. The surface figure of the assembled mirror with 20 piezostack bonded actuators is demonstrated and a laser-induced damage threshold tested with a witness sample is also reported.
収録刊行物
-
- SPIE Proceedings
-
SPIE Proceedings 9983 99830B-, 2016-07-22
SPIE