Strength of 2017 aluminium alloy stud joints by friction welding

DOI

Search this article

Description

Stud joints of 2017 aluminium alloy were friction welded and its joint strength was examined. A stair zone was formed at the weld interface. Although the hardness of the stair zone was almost the same as base metals, the heat-affected zone of the bar and the plate was softened. The tensile strength of joints tended to increase with a pressure and a friction time, and the highest tensile strength was 275 MPa (63.1% joint efficiency for the bar base metal). In the bending testing, joints were cracked in the weld zone at a bending angle of less than 5°. In the fatigue testing, joints fractured near the weld interface and the fatigue strength of joints increased as the tensile strength of joints was high.