Incoherent High-Resolution Z-Contrast Imaging of Silicon and Gallium Arsenide Using HAADF-STEM

DOI

Search this article

Description

<jats:title>Abstract</jats:title><jats:p>The high-angle annular dark-field (HAADF) technique in a dedicated scanning transmission electron microscope (STEM) provides strong compositional sensitivity dependent on atomic number (Z-contrast image). Furthermore, a high spatial resolution image is comparable to that of conventional coherent imaging (HRTEM). However, it is difficult to obtain a clear atomic structure HAADF image using a hybrid TEM/STEM. In this work, HAADF images were obtained with a JEOL JEM-2010F (with a thermal-Schottky field-emission) gun in probe-forming mode at 200 kV. We performed experiments using Si and GaAs in the [110] orientation. The electron-optical conditions were optimized. As a result, the dumbbell structure was observed in an image of [110] Si. Intensity profiles for GaAs along [001] showed differences for the two atomic sites. The experimental images were analyzed and compared with the calculated atomic positions and intensities obtained from Bethe's eigen-value method, which was modified to simulate HAADF-STEM based on Allen and Rossouw's method for convergent-beam electron diffraction (CBED). The experimental results showed a good agreement with the simulation results.</jats:p>

Journal

  • MRS Proceedings

    MRS Proceedings 589 1999-01-01

    Springer Science and Business Media LLC

Details 詳細情報について

Report a problem

Back to top