<jats:title>ABSTRACT</jats:title><jats:p>Preparation of a sigma-CrFe single-phase specimen was achieved by arc melting of pure Fe and Cr, cold rolling, and subsequent annealing at 973 K or 1073 K in vacuum. Cold rolling before annealing is effective for the annealing-induced formation of sigma-CrFe from the bcc solid-solution phase. The phase stability and the structural change from sigma-CrFe to a bcc solid-solution phase under fast electron irradiation were investigated by in situ transmission electron microscope (TEM) observation in the temperature range between 22 K and 473 K by using an ultra-high voltage electron microscope (UHVEM). The phase transition of sigma-CrFe by fast electron irradiation was found to occur at a particular temperature.</jats:p>