しぼ付け加工を可能とする合成皮革の研究

書誌事項

タイトル別名
  • シボツケ カコウ オ カノウ ト スル ゴウセイ ヒカク ノ ケンキュウ
  • Investigating wrinkle formation on synthetic leather

この論文をさがす

抄録

In this study, 1,6-hexanediol(HD)and isosorbide(ISB), which is a biomass raw material, were used as glycols in the production of polycarbonate diol(PCD). Polyurethane(PU)resin obtained from these polyols was employed as the skin layer of synthetic leather to assess its suitability for wrinkle processing and durability. PU resins for synthetic leather adhesives were prepared both with and without a crosslinking agent, and the presence of wrinkles after reheating was confirmed. We observed that wrinkle formation was achievable using PU containing ISB-PCD. Moreover, this PU for wrinkle processing exhibited a yield point at temperatures in the range of 20℃–40℃ and a high glass transition temperature(Tg). Furthermore, their durability fell within a practical range. In contrast, synthetic leather produced by adding a crosslinking agent to the PU resin for adhesives resulted in deep wrinkles that persisted even after reheating following the crosslinking reaction, confirming the long-term durability of the wrinkles.

identifier:http://repo.kyoto-wu.ac.jp/dspace/handle/11173/3869

収録刊行物

  • 生活造形

    生活造形 069 70-75, 2024-02-29

    京都女子大学生活造形学科

詳細情報 詳細情報について

問題の指摘

ページトップへ