Models for ultrasonic characterization of environmental degradation of interfaces in adhesive joints

DOI PDF 被引用文献1件
  • A. I. Lavrentyev
    Nondestructive Evaluation Program, The Ohio State University, 190 West 19th Avenue, Columbus, Ohio 43210
  • S. I. Rokhlin
    Nondestructive Evaluation Program, The Ohio State University, 190 West 19th Avenue, Columbus, Ohio 43210

書誌事項

公開日
1994-10-15
DOI
  • 10.1063/1.357301
公開者
AIP Publishing

この論文をさがす

説明

<jats:p>In this paper we discuss two models of environmental degradation of adhesive joints developed from experimental observation of the joint failure mode. It is found that after severe degradation, failure is dominated by the interfacial mode, i.e., by failure at the interface between adhesive and adherend. The fraction of failure in the interfacial mode was found to be related to the joint strength and to be proportional to the frequency shift of a minimum in the spectrum of the reflected ultrasonic signal. One model considers an interface as an interphase in the form of a nonhomogeneous layer composed of two phases: ‘‘soft’’ which is viscoelastic (degraded part of the interphase) and ‘‘stiff’’ corresponding to the nondamaged interphase. Increase of the ‘‘soft’’ phase fraction corresponds to the process of degradation in the interphase. The second model describes degradation in a form of disbonds filled by absorbed water at the interface. The disbonded interface is modeled by transverse spring boundary conditions, with the complex spring stiffness representing the quality of the bond. The influence of different disbond growth scenarios is considered. Advantages and drawbacks of these models are discussed.</jats:p>

収録刊行物

被引用文献 (1)*注記

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ