- Diamond film characterization by analyzing C 1s peak shapes with X-ray photo-electron spectroscopy.
- Xセン コウデンシ ブンコウホウ ニ オケル C1s スペクトル ハケイ カイ
この論文をさがす
抄録
Characterization of diamond films by XPS was carried out by measuring the FWHM (full width at half maximum) and the peak shape of a core C 1s spectrum, and this method was also applied to other carbon films. C 1s peak shapes of natural diamond, graphite carbon, amorphous carbon, glassy carbon, polyethylene (PE) and diamond films formed by the CVD method were analyzed. The C 1s peaks of natural diamond and diamond films showed the same FWHM value, i.e., the diamond films had diamond structure. While the C 1s peak of the natural diamond was symmetric, and those of the other carbon samples were asymmetric. The C 1s peak shape of diamond films was similar to that of amorphous-carbon containing C-H bonds. As a result, it was found that the diamond films contain the C-H bonds in their structure.
収録刊行物
-
- 分析化学
-
分析化学 42 (3), 133-140, 1993
公益社団法人 日本分析化学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001204051866112
-
- NII論文ID
- 110002906536
-
- NII書誌ID
- AN00222633
-
- COI
- 1:CAS:528:DyaK3sXktlSqtbs%3D
-
- NDL書誌ID
- 3810483
-
- ISSN
- 05251931
- http://id.crossref.org/issn/05251931
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- NDL-Digital
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可