イオン注入法による鉄鋼,Al合金の表面改質

書誌事項

タイトル別名
  • A study of surface modification of steel, Al alloy by ion implantation technique.

抄録

The effect on the metallurgical structure and wear behavior of Al-Si alloy and steel produced by nitrogen ion implantation and ion beam mixing deposition (simultaneous nitrogen ion implantation and Ti vapor deposition) using an ion beam source were studied. A combination of X-ray diffraction, Auger electron spectroscopy (AES) and X-ray photoelectron spectroscopy (XPS) was used to determine the metallurgical structure and chemical composition, and to investigate. The chemical bonding state of the ion treated surfaces.<br>X-ray diffraction data showed that TiN films were formed at room temperature by ion beam mixing treatment. It is demonstrated, that a mixing layer was observed between the substrate and TiN film.<br>AlN was observed when nitrogen ions were implanted in Al-Si alloy. The pin-on disk wear test showed a decrease in the coefficient of friction and an increase in wear resistance for surface treated by both nitrogen ion implantation and ion beam mixing.

収録刊行物

  • 金属表面技術

    金属表面技術 38 (8), 329-333, 1987

    一般社団法人 表面技術協会

被引用文献 (1)*注記

もっと見る

詳細情報 詳細情報について

  • CRID
    1390001204111818368
  • NII論文ID
    130003810108
  • DOI
    10.4139/sfj1950.38.329
  • COI
    1:CAS:528:DyaL2sXlsF2msr0%3D
  • ISSN
    18843395
    00260614
    http://id.crossref.org/issn/00260614
  • 本文言語コード
    ja
  • データソース種別
    • JaLC
    • Crossref
    • CiNii Articles
  • 抄録ライセンスフラグ
    使用不可

問題の指摘

ページトップへ