- HIRAI Kazumasa
- Graduate School, Waseda Univ.
-
- FUWA Akio
- School of Sci. & Eng., Waseda Univ.
Bibliographic Information
- Other Title
-
- 金めっき膜に対する素地ニッケル結晶面の影響
- キン メッキ マク ニ タイスル キジ ニッケル ケッショウメン ノ エイキョ
Search this article
Description
The effect of the crystal structure of various nickel substrates on the orientation of plated gold films was studied. The gold plating was conducted in a solution primarily composed of gold potassium cyanide at 338K and pH=6.5 with a current density of 5mA/cm2. It was found that the crystal structure of the nickel substrate influenced the orientation of the gold film as follows: (i) for films thinner than 0.2μm, there was epitaxial growth of gold film on the nickel substrate as (111)Au||(111)Ni, (200)Au||(200)Ni and (220)Au||(220)Ni: (ii) for films between 0.2 and 3μm, there was growth of the (110) plane of gold on the nickel substrates; and (iii) for films thicker than 3μm, the growth plane orientations were (111)>(220)>(200), which is considered the characteristics of gold plating under these condition.
Journal
-
- Journal of The Surface Finishing Society of Japan
-
Journal of The Surface Finishing Society of Japan 43 (9), 868-872, 1992
The Surface Finishing Society of Japan
- Tweet
Details 詳細情報について
-
- CRID
- 1390001204114904960
-
- NII Article ID
- 130001072681
-
- NII Book ID
- AN1005202X
-
- COI
- 1:CAS:528:DyaK38Xmtlyjtrs%3D
-
- ISSN
- 18843409
- 09151869
-
- NDL BIB ID
- 3785946
-
- Text Lang
- ja
-
- Data Source
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- Abstract License Flag
- Disallowed