Simulation of Quenching Crack Generation in Low Alloy Cast Steel by Using Heat-treatment CAE Software

DOI IR HANDLE Web Site

Bibliographic Information

Other Title
  • 熱処理ＣＡＥソフトウェアを活用した低合金鋳鋼材の焼割れ発生シミュレーション
  • ネツ ショリ CAE ソフトウェア オ カツヨウ シタ テイゴウキン チュウコウザイ ノ ヤキワレ ハッセイ シミュレーション

Search this article

Abstract

In order to understand the quenching crack phenomenon in cast steel, a disk shaped low alloy cast steel specimen having a opening was quenched in water at 1123K. The behavior of a quench crack was investigated by microstructure observation and analyzed by the Heat treatment CAE software. The results obtained are as follows. (1) The quench cracking easily occured as the volume of specimen increased. The mass effect for quenching crack was significant. (2) The quench cracking was due to time lag in martensitic transformation at surface side and inner side of the quenched specimen, but not due to the thermal stress in the specimen. (3) The behavior of a quenching crack was able to be predicted by the Heat treatment CAE software. (4) Therefore, the Heat treatment CAE software is useful for a counterplan preventing the quenching crack.

Journal

Keywords

Details 詳細情報について

Report a problem

Back to top