懸濁紡糸法によるＭｇＢ２線材の作製

DOI Web Site 参考文献28件

書誌事項

タイトル別名
  • Fabrication of MgB2 Wire by Suspension Spinning
  • ケンダク ボウシホウ ニ ヨル MgB2 センザイ ノ サクセイ

この論文をさがす

説明

Suspension spinning of commercially available MgB2 powder was examined to fabricate a long superconducting MgB2 wire. The MgB2 powders were suspended in a nonaqueous poly(vinyl alcohol) solution. The viscous spinning dope was extruded as a filament into a precipitating medium of methyl alcohol and coiled on a winding drum. The as-drawn filaments were pressed and heated in order to remove volatile compounds. The filamentary samples were then cold-pressed, enveloped by an iron sheet with a pellet of mixed powder of Mg and B or with Mg powders, vacuum-sealed in a fused quartz tube and sintered. The Jc of the sample was strongly dependent on the starting materials and sintering condition. Although the transport Jc value was low, such as 4500 A/cm2 at 4.2 K and self-fields, a Jc value of more than 200 A/cm2 was maintained by applying a field of 10 T. Doping of 5 at% nanoscale SiC resulted in an improvement in the Jc and superconductivity at 4.2 K was maintained by applying a field of 14 T.

収録刊行物

  • 低温工学

    低温工学 38 (11), 589-595, 2003

    公益社団法人 低温工学・超電導学会 (旧 社団法人 低温工学協会)

参考文献 (28)*注記

もっと見る

キーワード

詳細情報 詳細情報について

問題の指摘

ページトップへ