摩擦圧接を用いた6191アルミニウム青銅スタッド継手の強度

書誌事項

タイトル別名
  • Strength of 6191 aluminum bronze stud joints by friction welding
  • マサツ アッセツ オ モチイタ 6191 アルミニウム セイドウ スタッド ツギテ ノ キョウド

この論文をさがす

抄録

Stud joints of C6191 aluminum bronze were friction welded and its joint strength was examined. A hardened stir zone formed at the weld interface and its width increased with a friction time. In the tensile testing, since all friction welded joints fractured in the plate side, friction weldability of C6191 stud joints was good. Contrary, arc stud welded joints fractured at the weld zone and there were blowholes. In the bending testing, friction welded joints were fractured near the weld zone at bending angle of about 5°. In the fatigue testing, friction welded joints fractured near the weld zone and the fatigue limits of joints were 90-115MPa.

収録刊行物

  • 圧力技術

    圧力技術 49 (5), 225-231, 2011