化学的共沈法によるＣｏ‐Ｎｉ‐Ｍｎスピネル系微粒子の作製条件による諸特性
書誌事項
- タイトル別名
-
- Some Properties of Co-Ni-Mn Spinel Ferrite Fine Particles Prepared by the Chemical Coprecipitation Method with Various Preparation Conditions
- 化学的共沈法によるCo-Ni-Mnスピネル系微粒子の作製条件による諸特性
- カガクテキ キョウチンホウ ニ ヨル Co Ni Mn スピネルケイ ビリュウシ ノ サクセイ ジョウケン ニ ヨル ショトクセイ
この論文をさがす
説明
An experiment was carried out to investigate the effect of MnO substitution, mole ratio n { = Fe3+/(Co2++Ni2++Mn2+)}, reaction temperature, and concentration of alkali on the magnetic and physical properties of Co-Ni-Mn ferrite prepared by the chemical coprecipitation method without post-annealing. The chemical coprecipitation compositions were chosen according to the formula (CoO)0.5(NiO)0.5-x(MnO)x·n/2(Fe2O3), where x varied between 0 and 0.5 and n varied between 1.80 and 2.00. To remove the superparamagnetic substance, the coprecipitation fine particles were etched with dilute sulfuric acid. As a result, in the (CoO)0.5(NiO)0.3(MnO)0.2·1.95/2(Fe2O3) composition, when the reaction temperature and excess NaOH were 60°C and 0.5 mol, the following magnetic and physical properties were obtained: saturation magnetization σs = 79.77×10-6 Wb·m/kg, residual magnetization σr = 47.38×10-6 Wb·m/kg, coercivity HcJ = 184 kA/m, and average particle size D = 19.61 nm.
収録刊行物
-
- 日本応用磁気学会誌
-
日本応用磁気学会誌 31 (4), 322-327, 2007
公益社団法人 日本磁気学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205092462592
-
- NII論文ID
- 110006317636
-
- NII書誌ID
- AN0031390X
-
- COI
- 1:CAS:528:DC%2BD2sXhtVWqs7bO
-
- ISSN
- 18804004
- 02850192
-
- NDL書誌ID
- 8879069
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDLサーチ
- Crossref
- NDLデジコレ（旧NII-ELS）
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可