高速連続鋳造時の鋳型内潤滑・伝熱挙動

書誌事項

タイトル別名
  • Behavior of Lubrication and Heat Transfer in Mold at High Speed Continuous Casting
  • コウソク レンゾク チュウゾウジ ノ イガタナイ ジュンカツ デンネツ キョド

この論文をさがす

抄録

In order to cast high quality slabs with high productivity, high speed casting technology has been investigated with a pilot continuous casting machine capable of casting 50 to 100 tons of molten steel. The results can be summarized as follows;<BR>(1) High casting speed of 5.0 m/min for low carbon steel has been achieved with low viscosity powder. The powder consumption is small, from 0.1 to 0.2 kg/m2, but stable casting has been conducted.<BR>(2) Longitudinal crack has been occured even if for low carbon steel at up to 4.0 m/min. When the heat flux in mold increased critical value, longitudinal crack occured.<BR>(3) The control of the heat fluxes through the mold can be achieved by using the powder with appropriate properties.

収録刊行物

  • 鉄と鋼

    鉄と鋼 83 (11), 701-706, 1997

    一般社団法人 日本鉄鋼協会

被引用文献 (14)*注記

もっと見る

参考文献 (15)*注記

もっと見る

詳細情報 詳細情報について

問題の指摘

ページトップへ