- Characterization of Carbon Thin Films Prepared by High Power Impulse Magnetron Sputtering
- ダイ デンリョク パルスマグネトロンスパッタ オ モチイタ タンソケイ ハクマク ノ トクセイ
この論文をさがす
抄録
The characteristics of diamond-like carbon (DLC) films deposited by high power impulse magnetron sputtering (HiPIMS) with multipolar magnetic plasma confinement (MMPC) were investigated. DLC films were prepared on silicon (Si) by HiPIMS and HiPIMS-MMPC over varying substrate bias voltage. Depositions were performed from a graphite target (210 mm in diameter) under argon (Ar) gas atmosphere at chamber pressure of 0.5 Pa. The DLC films were analyzed by several methods. In HiPIMS-MMPC, the peak power density was approximately 690 W/cm2 at a duty cycle of 1% (frequency: 200 Hz). According to Raman spectroscopy, the structure of DLC film deposited by HiPIMS-MMPC could be changed from amorphous carbon (a-C) to tetrahedral amorphous carbon (ta-C). The deposition rate in HiPIMS-MMPC was approximately 50% (10 nm/min) lower than that in HiPIMS. However, HiPIMS-MMPC is considered as one of the effective methods to prepare hard and dense DLC films (20 GPa and 2.00 g/cm3 at the maximum).<br>
収録刊行物
-
- Journal of the Vacuum Society of Japan
-
Journal of the Vacuum Society of Japan 60 (9), 341-345, 2017
一般社団法人 日本真空学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205296059264
-
- NII論文ID
- 130006077262
-
- NII書誌ID
- AA12298652
-
- ISSN
- 18824749
- 18822398
-
- NDL書誌ID
- 028531310
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可