書誌事項
- タイトル別名
-
- Fracture energy of MgO-SiC whisker composite ceramics.
- MgO SiC ウイスカー フクゴウ セラミックス ノ ハカイ エネルギ
この論文をさがす
抄録
In order to develop MgO base ceramics having higher thermal shock resistance for MHD plant use, ceramic composites of MgO reinforced with 15 and 20wt% of SiC whisker were fabricated by the hot-pressing at 1800°C and 1900°C under 200kg/cm2 for 30min. The effective fracture energy (γeff) of the hot-pressed composites and MgO were measured by work of fracture technique using chevron notched specimens over the range from room temperature to 1400°C. Up to 1000°C, the γeff values of the composite ceramics were slightly lager than those of the hot-pressed MgO. At temperatures above 1000°C, the γeff values of the composites increased remarkably, and were about 3-7times higher than those of hot-pressed MgO at 1400°C.<br>The mechanism of the increase in γeff values were discussed on the basis of the load-deflection behavior in bending fracture, the chemical reaction of SiC whisker with MgO matrix and the fracture surface morphology.
収録刊行物
-
- 材料
-
材料 36 (400), 17-21, 1987
公益社団法人 日本材料学会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205391111168
-
- NII論文ID
- 110002296988
-
- NII書誌ID
- AN00096175
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 3119052
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可