- Structural Control of Porous Fly-Ash and Flexural Strength by Zeolitization
- タコウシツ フライアッシュ ノ ソシキ セイギョ ト ゼオライトカ ニ ヨル キョウド ヘンカ
この論文をさがす
説明
The porous fly-ash ceramics with various porosity were prepared using colloidal process with molten wax. Polyethylene terephthalate powders were used combustible pore-forming agents. The total porosity of porous fly-ash increased with the polyethylene terephthalate powder content. The flexural strength of porous fly-ash drastically decreased as the total porosity increased. By the treatment of the sintered fly-ash with 3mol/dm3 NaOH solution at 383K for 15h, phillipsite, a kind of zeolite, was formed on the sintered fly-ash surface. The flexural strength of sintered fly-ash decreased to half of the original value by the zeolitization treatment.
収録刊行物
-
- 材料
-
材料 52 (6), 601-605, 2003
公益社団法人 日本材料学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001205419506560
-
- NII論文ID
- 110002302142
-
- NII書誌ID
- AN00096175
-
- COI
- 1:CAS:528:DC%2BD3sXlsVygtrc%3D
-
- ISSN
- 18807488
- 05145163
-
- NDL書誌ID
- 6617640
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDLサーチ
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可