- G0601-7-6 Thermal Decomposition Behavior of Plastics with Flame Retardant under Constant Temperature Condition
抄録
In order to develop effective final treatment system of waste plastics, thermal gasification characteristics of plastics compounds containing flame retardant were investigated. Polypropylenes (PP) which contained Al(OH)_3 or (NH_4PO_3)_n as a flame retardant were decomposed and burned under constant temperature condition in an image furnace while changing O_2 concentration from 0% to 21%. Mass reduction during thermal decomposition was measured by an electric-micro balance. The gas components produced by the thermal decomposition and combustion process were analyzed with a gas analyzer. It was found that HC concentration for PP was the highest at 10% oxygen concentration when the ambient temperature Τ_a was 1073K. CO_2 concentration for PP contained 20wt% Al(OH)_3 was higher than PP under 21% oxygen concentration.
収録刊行物
-
- 年次大会講演論文集
-
年次大会講演論文集 2009.3 (0), 77-78, 2009
一般社団法人 日本機械学会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206063445504
-
- NII論文ID
- 110007861728
-
- ISSN
- 24331325
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可