The pitting corrosion and hydrogen absorption embrittlement of Zr in fractionating tower handling HCl solution were discussed. The corrosion rate of Zr in the 20% boiling HCl tended to be increased by the addition of a trace of HF (1ppm). Then, it became clear by the analysis of operating solution that the corrosion of tower was attributable to the presence of F in this solution. The carbon was also used in this plants for heat exchanger tube, then local corrosion of Zr was accelerated by the galvanic action when it was in contact with the carbon chips. The thermally oxidized film of Zr acted as protective for corrosion, but when its film was locally broken, the corrosion rate of breaked areas were accelerated in the presence of HF.
収録刊行物
-
- CORROSION ENGINEERING
-
CORROSION ENGINEERING 39 (3), 119-124, 1990
社団法人 腐食防食協会
- Tweet
詳細情報 詳細情報について
-
- CRID
- 1390001206257622784
-
- NII論文ID
- 130004732161
- 130006025307
-
- NII書誌ID
- AN00225595
-
- ISSN
- 18841155
- 00109355
-
- NDL書誌ID
- 3655463
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可