- Corrosion Resistance for Various Kinds of Materials under Molten Carbonate Fuel Cell Environment
- ヨウユウ タンサンエンガタ ネンリョウ デンチ カンキョウチュウ ニ オケル
この論文をさがす
抄録
Corrosion resistance for various kinds of materials was investigated under molten carbonate fuel cell environment at 650°C. In addition, anodic polarization measurements and free corrosion potential measurements for several pure metals and stainless steels were carried out in molten carbonate. Ni and aluminized stainless steels showed good corrosion resistance to molten carbonate under fuel gas environment, and Cr was also an effective element to improve the corrosion resistance in this environment. On the other hand austenitic stainless steels such as SUS 316 L and SUS 310 showed fairly good corrosion resistance to molten carbonate under oxidant gas environment because protective oxide films were formed on the surfaces. The results obtained from electrochemical measurements were well consistent with those of conventional weight loss measurements. Therefore, electrochemical measurements are considered to be an effective method to evaluate the corrosion resistance of metals in molten carbonate.
収録刊行物
-
- CORROSION ENGINEERING
-
CORROSION ENGINEERING 36 (7), 438-444, 1987
社団法人 腐食防食協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001206258401408
-
- NII論文ID
- 130004731955
- 130006025191
-
- NII書誌ID
- AN00225595
-
- ISSN
- 18841155
- 00109355
-
- NDL書誌ID
- 3145222
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可